名称：Ti3C2自支撑膜
状态：黑色圆形
制备工艺：真空抽滤
直径：40 mm
厚度：7-15um
说明：Ti3C2自支撑膜可弯曲，具有脆性，收到货物小心拆包。因产品为纯手工制作，不能保证绝对平整，敬请谅解。
应用领域：柔性电子器件（传感器、电容器），柔性电池等，可用于沉积负载其他材料做复合材料以及海水分离的分离膜
储存条件：常温干燥惰性气体密闭保存，最长保存期限 3 个月。

MXenes材料 MXenes material
	名称 Product name	工艺 Processing technology	具体细节 Details
Ti2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
Nb2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 Cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
V2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
Ti3C2	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	黏土材料 Clay materials	LiF处理 LiF Treatment	黏土材料，经超声离心可分散为单层材料，产率约为25-35%。超声功率需160W以上，时间约为2h到6h。 Clay material, which can be dispersed as a single layer material by ultrasonic centrifugation, yields about 25-35%. Ultrasound power needs more than 160W, and the time is about 2 h to 6 h.
	单/少层胶体溶液 Single/Layer Colloidal Solution	5mg/ml 100ml	单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.
	单/少层胶体溶液 Single/Layer Colloidal Solution	10mg/ml 100ml	单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.
	单/少层粉末材料 Single/Layer Powder Material	冷冻干燥 freeze drying	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。 Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
	自支撑膜材料 Self-supporting membrane materials	真空抽滤 Vacuum suction filtration	单/少层村料的胶体溶液，经过真空抽滤得到的柔性膜。Flexible membranes obtained from the colloidal solution of single/small-layer village materials by vacuum filtration.

具体表征请见附件：MXene手册