Monolayer colloidal aqueous solution Ti2C MXenes

product information:
Name: Single-layer colloidal solution Ti2CTx MXenes
Functional group: -OH-F-O-Cl (customizable)
Size: less than 500nm less than 200nm less than 100nm less than 50nm
Purity:99%
Storage conditions: low temperature, dry and sealed, must be stored in an inert atmosphere

Process: HF treatment or HCl+LiF treatment

MXenes材料 MXenes material
	名称 Product name	工艺 Processing technology	具体细节 Details
Ti2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
Nb2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 Cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
V2C	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	单/少层粉末材料 Single/Layer Powder Material	冷冻处理 cryogenic treatment	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
Ti3C2	风琴状 Organoid material	HF处理 HF Treatment	风琴状材料，由氢氟酸刻蚀得到。 Organ-like material obtained by etching with HF.
	黏土材料 Clay materials	LiF处理 LiF Treatment	黏土材料，经超声离心可分散为单层材料，产率约为25-35%。超声功率需160W以上，时间约为2h到6h。 Clay material, which can be dispersed as a single layer material by ultrasonic centrifugation, yields about 25-35%. Ultrasound power needs more than 160W, and the time is about 2 h to 6 h.
	单/少层胶体溶液 Single/Layer Colloidal Solution	5mg/ml 100ml	单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.
	单/少层胶体溶液 Single/Layer Colloidal Solution	10mg/ml 100ml	单/少层村料的胶体溶液，具有丁达尔现象，可以直接利用的MXenes材料。 The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.
	单/少层粉末材料 Single/Layer Powder Material	冷冻干燥 freeze drying	单/少层村料的胶体溶液，经过冷冻干燥得到的粉末。 Powder obtained by freeze-drying of colloidal solution of single/small layer village material.
	自支撑膜材料 Self-supporting membrane materials	真空抽滤 Vacuum suction filtration	单/少层村料的胶体溶液，经过真空抽滤得到的柔性膜。Flexible membranes obtained from the colloidal solution of single/small-layer village materials by vacuum filtration.

具体表征请见附件：MXene手册