【Research Background】

        Two-dimensional transition metal carbon / carbonitride is a rising star in the 2D material family. MXenes are prepared by selective etching of A-atomic layer elements in the MAX phase, where A represents elements of Group 13-16 (Al, Si, etc.), and M represents pre-transition metal elements (TI, V, Nb, etc.). The general formula is: M n + 1 X n T x , T x represents surface functional groups such as -F, -O and -OH. Thanks to its unique 2D layered structure, hydrophilic surface and metal conductivity (> 6,000 S cm ^-1 ), MXenes has shown great potential in a wide range of applications, especially electrochemical storage Energy field. With the first report of Ti3C2 MXene in 2011, the main etching environment of MXenes is an aqueous solution containing fluoride ions, such as aqueous hydrofluoric acid, LiF + HCl or ammonium hydrogen fluoride. Up to now, the reactivity of Al, which is mainly derived from Al-containing MAX phase precursors, and fluorine-based aqueous solutions has limited the synthesis of MXenes. Although it has been reported that Si in Ti3SiC2 MAX phase is etched by oxidizer , the etching mechanism is still based on the use of corrosive HF solution. Therefore, the main challenges in the synthesis of MXene are mainly focused on: 1) finding a non-toxic synthetic route; 2) preparing a wider range of MAX phase precursors.

【Achievement Introduction】

Recently, Professor Huang Qing of Ningbo Institute of Materials Science , Chinese Academy of Sciences, Professor Patrice Simon of University of Toulouse, France, and Professor Lin Zifeng of Sichuan University published the title in the top international academic journal Nature Materials :  A general Lewis acidic etching route for preparing MXenes with enhanced electrochemical performance in non- Research paper on aqueous electrolyte . Different from the traditional method, the paper proposes a method for preparing MXenes by selective etching of A in the MAX phase of non-traditional A element using Lewis acid molten salt, and corresponding verification is carried out. Ti 3 C 2 MXene etched by this method has a reversible capacity of 738 C g ^-1 (205 mAh g ^-1 ) and a high coulombic efficiency when applied to lithium storage .

【Graphic introduction】

Figure 1.  Etching diagram ofMS-Ti 3 C 2 T x MXene.

Figure 2.   Microstructure and structure characterization of MS-Ti 3 C 2 T x MXene.

Figure 3. The  Lewis acid etching method expands the MAX phase family.

Figure 4.   Electrochemical performance test of MS-Ti 3 C 2 T x  MXene electrode in 1 M LiPF 6 electrolyte.

【Summary of this article】

 "Mirror-like" electrochemical storage combined with Li ⁺ insertion and extraction in non-aqueous Li ⁺ electrolyteThe energy mechanism, high capacity, high charge and discharge rate, and lower operating voltage (0.2-2.2 V vs. Li ⁺ / Li) make MXenes obtained by this unconventional etching method used as the negative electrode of electrochemical energy storage devices Has great potential (batteries and lithium-ion capacitors). This general Lewis acid etching method expands the range of MAX phase precursors and can prepare new MXenes materials, providing unprecedented possibilities for regulating the surface chemical properties of MXenes.